FC Anti-Oxidant Coating for Billet steel
    发布时间: 2017-06-19 10:51    

                                           FC  Anti-Oxidant Coating for Billet steel

 

    This  Shielding  coating mass is a new kind of  high technology refractory products :

   1.Traditional refractory products are mainly used for most furnace kilns , instead of this usage 

our anti-oxide coating is used for the end finished products -- the steel billet and steel ingot ;

   2. After studying and developing for the main refractory raw material : brown corrundom and

 Large crystall , we mix them according to new ratio ,and then we found new crystal phase .

 3.Through many experiences on the steel billet and steel ingot we test this kind of new crystal

 phase can refrain the steel billets from touching the air directly, prevent the steel billet and steel

 ingot from oxiding and decarbonizing . 

  

  Index:

  We studying and invent two kinds of coating mass according to steel billet ‘s PH kinds as following :

 

Item

specification

MgO

Al2O3

SiO2

Size

I-M     (Magnesia base) 

65%

15%

20%

0-200 mesh

      I--A     (Corrundom base) 

 

65%

27%

0-200 mesh

 

 

 

Performance :

1.prevent the steel billet and steel ingot from oxiding, decrease and refrain the forming for iron scale sinter ,

improve the output of the steel.

(1). Without  coating .

4.jpg

(2).After coating .

5.jpg

2.Reduce the burning loss at 30%-80%, enhance the steel quality ;

 

Item

specification

MgO

Al2O3

SiO2

Size

Magnesia base

65%

15%

20%

 

Corrundom base

 

65%

27%


 

3.debase the steel pit on the surface substantially ,lessen the polish and decorate;
4.Guard the steel against decarbonizing and alloy segregation, cut down the crazing 

  during steel ‘s cooling period ;

 

(1). Without  coating .

9.jpg

(2).After coating .

8.png

5.Depress the steel billet adjoin because of iron scale sinter, and then ensure the

 producing on the rails . 

 

Using method:

1.According to the scale of 1:0.4 to add the water ;

2.Mix them together for 5-8 minutes into pasty ;

3.Coating or spraying the mixture onto the surface of the steel billets or steel ingot, after cooling for ten minutes 

coating again , and then once more .

4.The thickness of the coating should be more than 2mm.